| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 膜塑收缩 | 80×80×3板材 | 2.0-2.5 | % | ||
| 比重 | ASTM D-792 | 1.29 | ||||
| 吸水率 | 23℃·24小时 | ASTM D-570 | 0.08 | % | ||
| 机械性能 | 洛氏硬度 | 23℃ | ASTM D-785 | 59 | M标度 | |
| 拉伸强度 | 23℃ | ASTM D-638 | 490 | kg/cm2 | ||
| IZOD冲击强度(1/8时宽) | 无缺口 | 23℃ | ASTM D-256 | 不破裂 | kg.cm/cm | |
| 无缺口 | -40℃ | ASTM D-256 | 160 | kg.cm/cm | ||
| 缺口 | 23℃ | ASTM D-256 | 6.4 | kg.cm/cm | ||
| 缺口 | -40℃ | ASTM D-256 | 5.0 | kg.cm/cm | ||
| 弯曲模量 | 23℃ | ASTM D-790 | 23 | kg/cm2×103 | ||
| 弯曲强度 | 23℃ | ASTM D-790 | 770 | kg/cm2 | ||
| 断裂拉伸伸长 | 23℃ | ASTM D-638 | >150 | % | ||
| 负荷下的 | 4.6kg/cm | ASTM D-648 | 154 | ℃ | ||
| 18.6kg.cm | ASTM D-648 | 56 | ℃ | |||
| 洛氏硬度 | 23℃ | ASTM D-785 | 108 | R标度 | ||