L326 斯米克银焊条

Wire & rod
丝

650-720

Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等

BAg-34

L400 斯米克银焊条

Cast rod, wire & rod
铸条、丝

577-582

Si11.5
Al Rem.

Brazing of aluminum and aluminum alloys.
铝及铝合金的钎焊

BAlSi-4

L401斯米克银焊条

Cast rod
铸条

525-535

Si5 Cu28
Al Rem.

Brazing of aluminum and aluminum alloys.
铝及铝合金的钎焊

L600 斯米克银焊条

Wire & rod
丝

183-185

Sn60 Sb≤0.8
Pb Rem.

Soldering of fusible metals and heat-treated part.
易熔金属及热处理件的钎焊

60Sn

L601 斯米克银焊条

Wire & rod
丝

183-227

Sn18 Sb2
Pb Rem.

Soldering of copper, copper alloys and galvanized iron plain sheet.
铜及铜合金、镀锌铁皮的钎焊。

18Sn

L602 斯米克银焊条

Wire & rod
丝

183-256

Sn30 Sb2
Pb Rem.

Soldering of copper, brass, copper alloys and galvanized iron plain sheet.
铜、黄铜、铁、镀锌铁皮的钎焊

30Sn

L603 斯米克银焊条

Wire & rod
丝

183-235

Sn40 Sb2
Pb Rem.

Soldering of copper, copper alloys, steel and zinc parts.
铜及铜合金、钢、锌制零件的钎焊

40Sn

L604 斯米克银焊条

Wire & rod
丝

183-222

Sn90 Sb≤0.15
Pb Rem.

Soldering of copper and steel for food and medicine field.
食品、医疗所需铜、钢等金属的钎焊

90Sn

L605 斯米克银焊条

Wire & rod
丝

232-240

Ag5 Sn95

Soldering of copper and steel for electrical and food field.
电器、食品所需铜、钢等金属的钎焊

L608 斯米克银焊条

Wire & rod
丝

295-305

Sn5.5 Ag2.5
Pb Rem.

Soldering of copper, copper alloys, steel and stainless steel.
铜及铜合金、钢及不锈钢的钎焊

L702 斯米克银焊条

Powder
粉

970-1000

Cr7 B3 Si4
Ni Rem.

Brazing of stainless steel under vacuum or protective atmosphere.
不锈钢真空或保护气氛钎焊

BNi-2

Trade-
Mark
牌 号

Equivalent to China Standard
相当国标

Characteristics & application
特性和用途

Equivalent to AWS
相当AWS

D 667 斯米克焊条

EDZCr-B-15

HRc≥48. Resistance to wear, gas corrosion and oxidation. Hardfacing of blast furnace hopper and cracker part.
HRc≥48，耐磨、耐气蚀、抗氧化。堆焊高炉料钟、破碎机件

D 802斯米克焊条

EDCoCr-A-03

HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter.
HRc38-47，耐热、耐蚀、耐磨。堆焊高温工件如热剪切刀刃

ECoCr-A

D 812斯米克焊条

EDCoCr-B-03

HRc45-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve.
HRc45-50，耐热、耐蚀、耐磨。堆焊高温工件如内燃机阀

ECoCr-B

D 822斯米克焊条

HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler.
HRc≥53，耐热、耐磨，但抗冲击性差。堆焊锅炉旋转叶轮

D 832斯米克焊条

EDCoCr-C-03

HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way.
HRc≥50，耐热、耐磨。堆焊高温工件如热轧导轨

ECoCr-C

D 842斯米克焊条

EDCoCr-D-03

HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die.
HRc28-38，耐蚀、抗热疲劳，具有加工硬化性。堆焊热锻模

Z 308斯米克焊条

EZNi

Pure nickel, excellent general properties. Used to weld thin cast iron part and repair welding machined surface, such as guided way of machine tool.
纯镍，综合性能好。铸铁薄件及加工面补焊用，如机床导卫

ENi-Cl

Z 408斯米克焊条

EZNiFe

Iron nickel, high strength and excellent ductility. Repair welding of important gray cast iron and nodular cast iron, such as cylinder cap.
镍铁，强度高、塑性好。重要灰铸铁及球铁焊补用，如汽缸盖

ENiFe-Cl

Z 508斯米克焊条

EZNiCu-1

Copper nickel, good machinability and bad crack resistance. Repair welding of sand hole and gray cast iron machined surface subject to no load.
镍铜，易加工，但抗裂性较差。不受力的灰铸铁加工面及砂眼补焊

ENiCu-B

Cu 107斯米克焊条

ECu

Red copper, atmosphere and sea water corrosion and excellent electric conductivity. Welding of red copper such as electrical copper row.
紫铜，耐大气，海水腐蚀，导电性好。紫铜焊接用，如导电铜排

ECu

Cu 207斯米克焊条

ECuSi

Silicon bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass.
硅青铜，耐蚀、强度高。铜、硅青铜及黄铜焊接用

ECuSi

Cu 227斯米克焊条

ECuSnB

Tin phosphor bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass.
锡磷青铜，耐蚀、强度高。铜、硅青铜及黄铜焊接用

ECuSn-C

Cu 237斯米克焊条

ECuAl

Aluminum bronze, wear and corrosion and high strength. Welding or surfacing of copper alloys.
铝青铜，耐磨、耐蚀，强度高。铜合金焊接或堆焊用

ECuAl-A2

Al 109斯米克焊条

TAl

Pure aluminum, excellent corrosion resistance and middle strength. Welding of pure aluminum.
纯铝，耐蚀性好，但强度不高，纯铝焊接用

E1100

Al 209斯米克焊条

TAlSi

Silicon aluminum, good crack resistance and wide range of usage. Welding of aluminum alloys other than aluminum magnesium alloys.
铝硅，抗裂性好，通用性大。铝合金焊接用，不宜焊接铝镁合金

E4043

Al 309斯米克焊条

TAMn

Manganese aluminum, corrosion resistance and high strength. Welding of aluminum alloys.
铝锰，强度高，耐蚀。铝合金焊接用

E3003

Ni 102斯米克焊条

ENi-1

Pure nickel. Welding and surfacing of nickel and nickel to steel.
纯镍，用于镍、镍与钢的焊接与堆焊

ENi-1

Ni 207斯米克焊条

ENiCu-7

Copper nickel. Welding and surfacing of copper nickel and copper nickel to steel.
镍铜，用于镍铜、镍铜与钢的焊接与堆焊

ENiCu-7

Trade
mark

牌 号

Chemical composition

主要成份(%)

Characteristics & application

特性和用途

Equivalent to AWS

相当AWS

S 101 斯米克焊丝

C3 Cr28 Ni4
Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，耐磨、耐气蚀、抗氧化。堆焊铲斗齿，泵套

S 111斯米克焊丝

C1 Cr29 W5
Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高温下耐磨、耐蚀。堆焊高温高压阀门

ECoCr-A

S 112斯米克焊丝

C1.5 Cr29 W8
Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高温下耐磨、耐蚀。堆焊阀门，热轧孔型

ECoCr-B

S 113斯米克焊丝

C2.5 Cr30 W17
Co Rem.

HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高温下耐磨、耐热，但抗冲击性差。堆焊螺旋送料机用

S 114斯米克焊丝

C2.5 Cr30 W12
Co Rem.

HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高温下耐磨、耐热，但抗冲击较差。堆焊牙轮钻头

ECoCr-C

S 201斯米克焊丝

Sn1 Si0.3Mn0.3
Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
机械性能好，抗裂性好。紫铜气焊及氩弧焊用

ERCu

S 211斯米克焊丝

Si3 Mn1
Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
机械性能好，铜合金氩弧焊及钢的MIG钎焊用

ERCuSi-Al

S 212斯米克焊丝

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。铜合金氩弧焊及钢的堆焊用

ERCuSn-A

S 213斯米克焊丝

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。铜合金氩弧焊及钢的堆焊用

ERCuSn-C

S 214斯米克焊丝

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

ERCuAl-A1

S 215斯米克焊丝

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

ERCuAl-A2

S 221斯米克焊丝

Cu60 Sn1 Si0.3
Zn Rem.

Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

S 221F斯米克焊丝

Cu60 Sn1 Si 0.3
Zn Rem.

S221 welding rod coated with flux.
外涂焊剂的S221焊丝

S 222斯米克焊丝

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

RBCuZn-C

S 222F斯米克焊丝

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

S222 welding rod coated with flux.
外涂焊剂的S222焊丝

RBCuZn-C

S 223斯米克焊丝

Cu59 Sn0.6
Zn Rem.

Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔点约900℃。铜、钢、铸铁钎焊用

RBCuZn-A

S 224斯米克焊丝

Cu62 Si0.5
Zn Rem.

Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

S 225斯米克焊丝

Cu48 Ni10
Zn Rem.

Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔点约935℃。高强度,钎焊钢、镍及硬质合金用

RBCuZn-D

S 225F斯米克焊丝

Cu48 Ni10
Zn Rem.

S225 welding rod coated with flux.
外涂焊剂的S225焊丝

RBCuZn-D

S 226斯米克焊丝

Cu60 Sn0.3
Si0.2 Zn Rem.

Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁

S 227斯米克焊丝

Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

RBCuZn-B

S 229斯米克焊丝

Cu55 Ni6 Mn4
Zn余

Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔点约920℃。高强度,钎焊钢、镍及硬质合金用

S 301斯米克焊丝

Al≥99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蚀。纯铝气焊、氩弧焊用

ER1100

S 311斯米克焊丝

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金

ER4043

S 321斯米克焊丝

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用

S 331斯米克焊丝

Mg5 Mn0.4
Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蚀，强度高。铝合金氩弧焊用

ER5183